POLYURETHANE 2K PAINT

AUTOMOTIVE 2K PAINT
Our 2K paints are high quality polyurethane lacquers that create glossy, hard surfaces, resistant to most chemicals and environmental conditions.

2 VERSIONS
Both lacquers are glossy and have identical resistance characteristics.
URKIVOC lacquer has the advantage of having low VOC levels.
Besa Nato lacquer (Universal adhesion)  has an exceptional ability to adhere directly to many types of materials: steel, stainless steel, galvanized, aluminum, brass, glass, plastic (ABS, PUR, PC, MA, GRP, PVC), ceramics, powder lacquer, coal coating

We offer 2 very hard lacquers with a wet effect:
- Polyurethane Glossy PU2K Standard (black or white at choice) (VOC <420g/L)
Offers:
298ml 2K Aerosol, White or Black
0.875L Kit: 500ml + 250ml hardener + 125ml thinner, White or Black
1.750L Kit: 1000ml + 500ml hardener + 250ml thinner, White or Black
8.500L Kit: 5000ml + 2.5L hardener + 1L thinner, White or Black

- Polyurethane Glossy Lacquer, Universal adehsion, PU2K-Besa Nato (Black) (VOC >420g/L - Product for professional use.)
Offers:
2K 298ml aerosol
0.875L Kit: 500ml + 250ml hardener + 125ml thinner
1.750L Kit: 1000ml + 500ml hardener + 250ml thinner
8.500L Kit: 5000ml + 2.5L hardener + 1L thinner
Destination: Cars, trucks, motorcycles

Mixture: 2:1 (100 parts paint to 50 parts hardener, 15-25% thinning)

Application: over a clean and primed surface, 1 medium pass followed 5-10 minutes after by a second very glossy coat.
Setting: 1.2 to 1.5mm nozzle.

Features: Solvent-based polyurethane lacquer. Two-component product (base and hardener). The drying and curing (polymerization) occur through the hardener. These products are finishes and therefore do not need additional top coat.

Chrome plating:
Our lacquers are perfect for creating undercoat for our plating solutions
When used for chrome plating, it is recommended to let the lacquers dry at least 72hrs (for chrome paint) or 24hrs (for chrome plating using the chrome machine), then treat them with a flame just before applying chrome plating.